Specifications |
Substrate material |
UV Grade Fused
Silica or BK7 |
Diameter |
25.0 +0~-.025 mm |
Thickness |
3 \ 0.5 mm |
Min. clear
aperture |
>85% of diameter |
Transmission |
>85% average
within specified range |
Attenuation |
>99% average
within specified range |
Angle of incidence |
0< \ 5< |
Coating Technology |
Electron
beam evaporation, dielectric multilayers |
LPF
Blockings |
From 80% of cut-on
λ to X-ray with the O.D. of 3 |
SPF Blockings |
From 120% of
cut-off λ to 1200nm(typical) with the O.D. of 3 |
Surface quality |
80/50 per
MIL-O-13830B |
Coating quality |
40/20 per
MIL-O-13830B |
Wedge |
<3 minutes |
Wavefront
distortion |
+1 wave @ 633nm
per 25mm |
Humidity
resistance |
Per MIL-C-675A |
Abrasion
resistance |
Per MIL-C-675A |
Optimum
temperature |
23<C |
Temperature limits |
-50<C to 100<C |
Certification |
Spectrophotometer
print of lot sample |
Cleaning |
Non-abrasive
method, isopropyl alcohol on lens tissue recommended |