Specifications |
Substrate material |
UV Grade Fused
Silica or BK7 |
Diameter |
25.0 +0~-.025 mm |
Thickness |
3 ¡À 0.5 mm |
Min. clear
aperture |
>85% of diameter |
Transmission |
>85% average
within specified range |
Attenuation |
>99% average
within specified range |
Angle of incidence |
0¡ã ¡À 5¡ã |
Coating Technology |
Electron
beam evaporation, dielectric multilayers |
Surface quality |
80/50 per
MIL-O-13830B |
Coating quality |
40/20 per
MIL-O-13830B |
Wedge |
<3 minutes |
Wavefront
distortion |
¡Ü1 wave @ 633nm
per 25mm |
Humidity
resistance |
Per MIL-C-675A |
Abrasion
resistance |
Per MIL-C-675A |
Optimum
temperature |
23¡ãC |
Temperature limits |
-50¡ãC to 100¡ãC |
Certification |
Spectrophotometer
print of lot sample |
Cleaning |
Non-abrasive
method, isopropyl alcohol on lens tissue recommended |
Laser Induced
Damage Threshold(LIDT) |
>5J/cm2
(1.06mm, 1ns) |
¡¡
LWT is able to provide the following long pass filters |
Part No. |
COWL
(nm) |
Attenuation
Range (nm) |
Wavelength
at 50% T (nm) |
Transmission
Range (nm) |
VIS-LPF400
|
400 |
340-380 |
400 ¡À10 |
440-1320 |
VIS-LPF450 |
450 |
380-430 |
450 ¡À10 |
495-1485 |
VIS-LPF500
|
500 |
425-475 |
500 ¡À10 |
550-1650 |
VIS-LPF550
|
550 |
470-525 |
550 ¡À10 |
605-1815 |
VIS-LPF600 |
600 |
515-575 |
600 ¡À10 |
660-1980 |
VIS-LPF650
|
650 |
550-620 |
650 ¡À10 |
715-2145 |
VIS-LPF700
|
700 |
600-670 |
700 ¡À10 |
770-2200 |
NIR-LPF750
|
750 |
640-715 |
750 ¡À10 |
825-2200 |
NIR-LPF800
|
800 |
685-760 |
800 ¡À10 |
880-2200 |
NIR-LPF850
|
850 |
725-810 |
850 ¡À10 |
935-2200 |
NIR-LPF900 |
900 |
770-860 |
900 ¡À10 |
990-2200 |
NIR-LPF950
|
950 |
810-910 |
950 ¡À10 |
1045-2200 |
NIR-LPF1000
|
1000 |
855-955 |
1000 ¡À10 |
1100-2200 |
NIR-LPF1100 |
1100 |
930-1050 |
1100¡À10 |
1150-2200 |
NIR-LPF1200 |
1200 |
1020-1150 |
1200¡À10 |
1250-2200 |
NIR-LPF1300 |
1300 |
1110-1250 |
1300¡À10 |
1350-2200 |
NIR-LPF1400 |
1400 |
1200-1350 |
1400¡À10 |
1450-2200 |
NIR-LPF1500 |
1500 |
1290-1450 |
1500¡À10 |
1550-2200 |
¡¡ |
¡¡ |
¡¡ |
¡¡ |
¡¡ |
¡¡ |